Polytetrafluoroethylene resin is white particles, with abnormal chemical stability, excellent electrical insulation, low friction coefficient, and excellent self-lubricating properties. The operating temperature range is -250℃～+260℃, and it can be used in the atmosphere for a long time. The nature does not change.

Product brand:

Brand	Application
4S01-A	Suitable for processing molded products such as plates and rods with high cleanliness requirements
4S01-B	Suitable for processing small and medium-sized molded products such as plates, rods, etc. with high cleanliness requirements
4S01-C	Suitable for processing ordinary molded products

Product performance:

Item	Index
	4S01－A	4S01－B	4S01－C
Tensile Strength,MPa ≥	25.5		22.5
Elongation at break，% ≥	250
Volume density,g/l	500±100
Average grainμm	180±80
Moisture content,% ≤	0.04
Melting point,℃	327±5
Standard relative density	2.13~2.18
Thermal instability index ≤	50
Electrical strength,MV/m	60		－

Packaging, storage, transportation:

1. The product is packed in a double-layer plastic bag and packed in a cardboard drum. The net content of each drum is 25kg.

2. The product should be stored in a clean, cool, and dry environment to avoid the mixing of dust, moisture and other impurities. Keep the container tightly closed during storage, and prevent the intrusion of dust and other impurities when opening the container.

3. This product is transported as non-dangerous goods. During transportation, avoid moisture, heat, severe vibration, and collision backlog to prevent resin from clumping.

Notes:

1. Before use, it should be placed in an environment of 22℃～25℃ for more than 24 hours to be sieved and pressed.

2. When this product is sintered, there should be an exhaust device to prevent inhalation of toxic gases. At the same time, high temperature processing above 390℃ should be avoided.